♦ GP-600 PTFE and Oil Lubricant with
Acrylic Packing
GP-600 Acrylic Packing by Made of
polyacrylonitrile filament through reinforcing,
braiding and impregnated with PTFE, having high
strength, wear-and impact -resistance, an ideal
substitute for asbestos packings, and
applicable for packing seal of pumps, valves
and vessels at a high linear speed and
pressure.
|
|
|
|
Pressure
|
Mpa
|
5
|
10
|
20
|
|
Temperature
|
℃
|
-100~250
|
|
Linear speed
|
M/s
|
2-12
|
|
PH range
|
2~12
|
|
Size
|
3mm ~ 50mm
|
GP-610 Acrylic Packing by Made of
polyacrylonitrile filament through reinforcing,
braiding and impregnated with PTFE, having high
strength, wear-and impact -resistance, an ideal
substitute for asbestos packings, and
applicable for packing seal of pumps, valves
and vessels at a high linear speed and
pressure.
|
|
|
|
Pressure
|
Mpa
|
5
|
10
|
20
|
|
Temperature
|
℃
|
-100~250
|
|
Linear speed
|
M/s
|
2-12
|
|
PH range
|
2~12
|
|
Size
|
3mm ~ 50mm
|
GP-620 Made from reinforced acrylic fiber, each
strand of yarn is sealed off with a special
grade of fine graphite flakes. In addition a
final coating of graphite is given to final
product prior to being squared. A direct
replacement for graphite asbestos packing
|
|
|
|
Pressure
|
Mpa
|
4
|
10
|
15
|
|
Temperature
|
℃
|
-100~260
|
|
Linear speed
|
M/s
|
2-10
|
|
PH range
|
2~12
|
|
Size
|
3mm ~ 50mm
|
|
|